metadata.dc.type: doctoralThesis
Title: Desenvolvimento de um novo compósito autoadesivo e antibiofilme aplicado como selante de fóssulas e fissufas
Other Titles: Development of a new composite autoadhesive and antibiofilm applied as sealant for fissures and fissures
metadata.dc.creator: Cocco, Alexandra Rubin
metadata.dc.contributor.advisor1: Piva, Evandro
metadata.dc.contributor.advisor-co1: Lund, Rafael Guerra
metadata.dc.contributor.advisor-co2: Koo, Hyun Michel
metadata.dc.description.resumo: A cárie dentária é uma doença oral crônica considetada multifatorial, e que atinge a maior parte da população mundial. As pessoas classificadas com maior risco de cárie são mais suscetíveis à doença. Sabe-se que os dentes posteriores, como molares e pré-molares, são os elementos dentários mais acometidos devido a sua anatomia, uma vez que possuem fóssulas e fissuras. Por isso, associações como a Academia Americana de Pediatria indicam o uso de selantes de fóssulas e fissuras como uma intervenção preventiva. Assim, essa tese de doutorado realizou uma revisão sistemática a fim de verificar quais tipos de tratamento de superfície em esmalte existem para aumentar a resistência de união dos selantes de fóssulas e fissuras, bem como quais tratamentos estão sendo realizados para substituir o ácido fosfórico. A tese visa, também, ao desenvolvimento de um selante resinoso autoadesivo contendo grupamentos metálicos, o di-nbutil-dimetacrilado de estanho ou o metacrilato de zinco, que foram incorporados em duas diferentes concentrações em massa: 2,5% e 5%, e a comparação com outros selantes de fóssulas e fissuras comerciais. De acordo com a revisão sistemática com meta-análise, vários tipos de tratamento de superfície do esmalte tem sido propostos como alternativas ao ácido fosfórico, como por exemplo, laser, primer or bond autoadesivos, selantes autoadesivos, abrasão/brocas, fosfato de caseína-fosfato de cálcio amorfo, re-ataque de ácido fosfórico, aplicação tópica de flúor entre outros, no entanto, há evidências apenas que a aplicacao prévia de primer ou bond autoadesivos podem melhorar a resistência de união dos selantes à base de resina. Acerca do desenvolvimento de um selante experimental autoadesivo, conclui-se que, quando comparado com os selantes comerciais, possui propriedades mecânicas inferiores; no entanto, quando comparado com uma resina flow autoadesivo, possui propriedades similares a superior. Uma vez adicionado os metacrilatos metálicos, verificou-se que a adição de 5% de di-n-butildimetacrilato de estanho mostrou ser efetivo em inibir a formação de bactérias (S. Mutans, S. Oralis) e de fungos (C. albicans). Chega-se à conclusão que foi possível desenvolver um selante à base de resina autoadesivo, ou seja, sem a utilização de ácido fosfórico e com propriedades antibiofilmes.
Abstract: Dental caries is a chronic oral disease considered multifactorial, affecting most of the world's population. People classified as higher caries risk are more susceptible to disease. In addition, posterior teeth such as molars and premolars are the most affected dental elements due to their anatomy that have pit and fissures. Therefore, associations such as the American Academy of Pediatrics indicate the use of pit and fissures sealants as a preventive intervention. Thus, this doctoral thesis has carried out a systematic review to verify what types of surface treatment in enamel exist to increase the bond strength of the sealants, as well as which treatments are being performed to replace the phosphoric acid. In addition, this thesis aims to develop a selfadhesive resin sealant and compare with other sealants and commercial fissures. In addition, the self-adhesive experimental sealant was characterized and two different metal monomers, tin di-n-butyl dimethacrylate and zinc methacrylate were incorporated in two different mass concentrations: 2.5% and 5%. According to the systematic review with meta-analysis, there are various types of surface treatment such as laser, primer or bond self adhesives, self-adhesive sealants, air-abrasion, casein phosphopeptideamorphous calcium phosphate, re-acid attack phosphoric, topical application of fluorine among others, however, there is evidence only self-ecthing primer or bond can improve the bond strength of the resin based sealants. On the development of a self-adhesive experimental sealant, it is concluded that when compared to commercial sealants it has lower mechanical properties, however, when compared with a self-adhesive flow resin, it has similar properties to the upper one. When added the metal methacrylates, it was found that the addition of 5% tin di-n-butyl dimethacrylate showed to be effective in inhibiting the formation of bacteria (S. Mutans, S. Oralis) and fungus (C. albicans). It is concluded that it was possible to develop a selfadhesive resin-based sealant, that is, without the use of phosphoric acid and with anti-biofilm properties.
Keywords: Materiais dentários
Efeito antibacteriano
Monômeros metálicos
metadata.dc.subject.cnpq: CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA
metadata.dc.language: por
metadata.dc.publisher.country: Brasil
Publisher: Universidade Federal de Pelotas
metadata.dc.publisher.initials: UFPel
metadata.dc.publisher.department: Faculdade de Odontologia
metadata.dc.publisher.program: Programa de Pós-Graduação em Dentística
Citation: RUBIN COCCO, Alexandra. Desenvolvimento de um novo compósito autoadesivo e antibiofilme aplicado como selante de fóssulas e fissuras. 2018. 191 p. Tese de Doutorado em Odontologia – Programa de Pós Graduação em Odontologia. Universidade Federal de Pelotas, Pelotas, 2018.
metadata.dc.rights: OpenAccess
URI: http://guaiaca.ufpel.edu.br:8080/handle/prefix/4279
Issue Date: 29-Jun-2018
Appears in Collections:PPGO: Dissertações e Teses

Files in This Item:
File Description SizeFormat 
Tese_Alexandra Rubin Cocco.pdf27,55 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons